Cooling for PMA (perpendicular magnetic anisotropy) enhancement of STT-MRAM (spin torque transfer-magnetic random access memory) devices

ABSTRACT

A fabrication process for an STT MTJ MRAM device includes steps of cooling the device at individual or at multiple stages in its fabrication. The cooling process, which may be equally well applied during the fabrication of other multi-layered devices, is demonstrated to produce an operational device that is more resistant to adverse thermal effects during operation that would normally cause a similar device not so fabricated to lose stored data and otherwise fail to operate properly.

BACKGROUND 1. Field of the Invention

This invention relates generally to a spin-torque transfer random access memory (STT-MRAM) device and to the application of thermal cooling to fabrication processes as a method of improving device performance.

2. Description

A critical aspect of MRAM performance is thermal stability, the ability of a device to maintain stored information stable against temperature variations without refreshing or other external help. It is especially important as the MTJ (magnetic tunnel junction) unit cell size scales down for advanced CMOS (complementary metal-oxide semiconductor) technology nodes since the thermal stability is proportional to the MTJ size in theory and positively correlated with the MTJ size in reality. In addition, some standard semiconductor assembly processes will expose the CMOS chips to high temperatures (260 C for example), with which MRAM, as a candidate for embedded memories, needs to comply. At such temperatures, the traditional thinking that thermal stability is solely the requirement of the free layer of a MTJ no longer applies. First, the temperature dependence of the thermal MTJ stability can be different for the free layer and the pinned layer as they may consist of different materials. Since the fabrication processing temperature is so much above the normal temperature range for typical data retention concerns, one cannot say the pinned layer has better thermal stability than free layer simply because it is within chip working temperature range (typically less than 125 C or 150 C) without additional study. More importantly, the free layer is normally at or near a balanced dipole field from the Synthetic Anti-Ferromagnetic (SAF) pinned layer, whereas the pinned layer is not. As temperature increases and coercivity field decreases, the difference between balanced and unbalanced dipole field can have a big influence on the thermal stability. As a result, one needs to consider thermal stabilities for both the free layer and pinned layer for embedded MRAM applications that follow the standard semiconductor product procedures.

As the film stacks for working MRAMs become more and more complicated and each functional layer tends to be formed of multiple layers of different materials for better performance, a single stack layer (i.e. a layer deposited using one set of deposition tool parameters, including targets, chamber pressure, gases and flow rates) is often ultra-thin, consisting only a few mono-atomic layers (a few Angstroms) of certain materials deposited across a 200 mm˜300 mm wafer. At this level, the films deposited in the MTJ stack have quite different properties than bulk materials and the deposition conditions can significantly change the morphology of the film, thus impacting the total MTJ performance, including thermal stability.

The conventional magnetic tunneling junction (MTJ) device is a form of ultra-high magnetoresistive device in which the relative orientation of the magnetic moments of parallel, vertically separated, upper and lower magnetized layers controls the flow of spin-polarized electrons tunneling through a very thin dielectric layer (the tunneling barrier layer) formed between those layers. When injected electrons pass through the upper layer their spins are polarized by interaction with the magnetic moment of that layer. The majority of the electrons emerge polarized in the direction of the magnetic moment of the upper layer, the minority being polarized opposite to that direction. The probability of such a polarized electron then tunneling through the intervening tunneling barrier layer into the lower layer then depends on the availability of states within the lower layer that the tunneling electron can occupy. This number, in turn, depends on the magnetization direction of the lower electrode. The tunneling probability is thereby spin dependent and the magnitude of the current (tunneling probability times number of electrons impinging on the barrier layer) depends upon the relative orientation of the magnetizations of magnetic layers above and below the barrier layer. The MTJ device can therefore be viewed as a kind of multi-state resistor, since different relative orientations (e.g. parallel and antiparallel) of the magnetic moments will change the magnitude of a current passing through the device. In a common type of device configuration (spin filter), one of the magnetic layers has its magnetic moment fixed in direction (pinned) by exchange coupling to an antiferromagnetic layer, while the other magnetic layer has its magnetic moment free to move (the free layer). The magnetic moment of the free layer is then made to switch its direction from being parallel to that of the pinned layer, whereupon the tunneling current is large, to being antiparallel to the pinned layer, whereupon the tunneling current is small. Thus, the device is effectively a two-state resistor. The switching of the free layer moment direction (writing) is accomplished by external magnetic fields that are the result of currents passing through conducting lines adjacent to the cell.

One of the deposition parameters that greatly influences the film property is the temperature of the wafer, which is a result of the fact that films grown on the wafer are generally the product of sputtering of various atomic species onto that wafer. When the sputtered species arrive at a cold surface, they tend to move and (or) penetrate less and vice-versa for arrival at a hot surface. Therefore, the result of the sputtering process depends on the affinity of the material being deposited and the material previously deposited. Using this fact, one can “tune” or adjust the wafer temperature to obtain some desired morphology (coverage, grain size, etc.) for the newly deposited film. This understanding leads us to the proposition that the very factors that challenge thermal stability of an operating device also play a role in the factors that affect the fabrication of that device. This understanding has led us and some of those in the prior art to suggest that thermal conditions that exist during device fabrication can affect the thermal stability of the final fabricated device. Examples of prior art attempts to regulate thermal conditions during fabrication to mitigate poor operational characteristics in the final device include the following.

U.S. Pat. No. 9,761,795 (Park et al.) discloses cooling a substrate in a cooling chamber to 50-300 K after the pinned layer is formed and before the MgO layer is formed. Cooling is by introducing a refrigerant into the chamber.

U.S. Patent Application 2013/0216702 (Kaiser et al.) teaches cooling a substrate in a cooling chamber to 50-293 K before or after part of the free layer has been formed.

U.S. Patent Application 2016/0130693 (Sawada et al) teaches cooling a substrate in a cooling chamber to room temperature before depositing a tunnel barrier layer.

U.S. Application 2016/0099288 (Watanabe et al) states that it is desirable for a cooling process to be performed before formation of the recording layer.

We have found that none of these approaches produce the results of the method to be disclosed herein.

SUMMARY

A first object of this disclosure is to provide an MRAM device with improved stability under thermal variations, i.e. the ability to maintain storage of data without refreshing cycles or other external assistance.

A second object of this disclosure is to provide such an MRAM device by means of a method of fabrication that lowers temperatures of the device being fabricated during certain portions of the fabrication process.

A third object of this disclosure is to address the issue of thermal stability by application of processing methods that will have the most advantageous affects on the properties of the thin films that are deposited on the wafers.

As we have noted above, one of the deposition parameters that greatly influences the film property is the temperature of the wafer. When a sputtered species arrives at a cold surface, it tends to move and (or) penetrate the surface less and vice-versa for arrival at a hot surface. Therefore, the result of the sputtering process depends on the affinity of the material being deposited and the material previously deposited. Using this fact, one can “tune” or adjust the wafer temperature to obtain some desired morphology (coverage, grain size, etc.) for the newly deposited film.

We find that by depositing part of the pinned layer at cool temperature in one of our presently used stacks, the thermal stability of the pinned layer, and therefore that of the chip as a whole, increases significantly and measurably.

This cooling is achieved inside a special cooling chamber within the deposition tool. After the initial part of the pinned layer deposition, the wafer is transferred in ultra-vacuum to the cooling chamber. It is then clamped to a cold stage (60 K) inside the chamber for certain period of time. The actual wafer temperature will decrease in the beginning of this process and reach a steady temperature close to that of the stage after approximately 200 s. Then the wafer is quickly transferred, while still in the ultra-vacuum, to the deposition chamber for the rest of the pinned layer deposition. The wafer temperature will slowly increase while still remaining cold during the rest of the pinned layer deposition.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a schematic representation of an MTJ MRAM stack that has been fabricated using the cooling process described herein.

FIG. 2 is a schematic representation showing the first step in the fabrication of the MTJ MRAM stack of FIG. 1.

FIG. 3 is a schematic representation showing the second step in the fabrication of the MTJ MRAM stack of FIG. 1.

FIGS. 4A-4C are a schematic representation showing three successive processes required to form a layer on the cooled fabrication during the third step in the fabrication of the MTJ MRAM stack of FIG. 1.

FIG. 5 is a schematic representation showing the fourth step in the fabrication of the MTJ MRAM stack of FIG. 1.

FIG. 6 is a schematic representation showing the fifth step in the fabrication of the MTJ MRAM stack of FIG. 1.

FIG. 7 is a schematic representation showing the sixth step in the fabrication of the MTJ MRAM stack of FIG. 1.

FIG. 8 is a schematic representation showing the final step in the fabrication of the MTJ MRAM stack of FIG. 1.

DETAILED DESCRIPTION

A preferred embodiment of the present disclosure is the fabrication of an exemplary STT MTJ MRAM cell fabricated with the imposition of temperature reduction (i.e., cooling) during any individual one of several steps in the process, or during several of the steps. We note that the process is by no means limited to the fabrication of an exemplary device such as this cell, but this particular device is one of importance in the industry and includes many commonly applied fabrication techniques, so the cooling process can be widely tested. The MRAM exemplary device is an MTJ layered structure (an unpatterned stack) that, upon completion, comprises the sequence of deposited layers shown schematically in FIG. 1. In FIGS. 2-8 we will describe and illustrate the nature of the individual deposition and cooling processes that ultimately create the stack in FIG. 1. We limit the fabrication process to be described using FIGS. 2-8 below to the application of a cooling step at one particular point in the fabrication, which is a step during the formation of the AP1 layer in a SAF (Synthetic Antiferromagnetic) pinned layer. In this step, the AP1 layer is being formed as two successively deposited layers, 44 and 42, and a cooling step is performed on layer 42 so that layer 44 can be deposited on cooled layer 42. It is to be understood that the cooling step can be performed at many other stages in the fabrication and the figures describing them would only differ in where the step is performed.

Referring then to FIG. 1, there is shown, schematically, the following final sequence of fabricated layers, whose individual properties will be discussed below. A wafer substrate 5 is provided as the base upon which the subsequent layers are fabricated. The substrate has been patterned (patterning not shown) to provide a surface region on which to fabricate the subsequent layers. The substrate will be removably affixed to various stages in the sputtering/deposition subsystem of a vacuum-sealed multi-chamber system that includes separate chambers configured for various types of depositions and processing. The multi-chamber system also includes a temperature-reducing thermal processing subsystem. We will describe this system in a bit more detail below.

On the substrate 5 there is formed a layer 7 of Ta or a conducting nitride such as TiN that is then surrounded by SiO2 and the whole is smoothed by a CMP (chemical mechanical polishing) process. This will afford a good contact for a subsequently deposited seed layer 10, on which is further formed a synthetic anti-ferromagnetically coupled (SAF) pinned layer 55, whose coupling is maintained by the RKKY (Ruderman-Kittel-Kasuya-Yosida) interaction. This coupled pinned layer system 55 itself comprises three layers: lower layer AP2, 20, RKKY interaction (or coupling) layer 30 and upper double layer AP1, 42/44. Note that AP1 layer is here formed of two sequentially deposited layers, denoted 42 and 44 which will be discussed further with respect to FIG. 4A-4C, below. The magnetic moments of layers AP1 and AP2 are held in an antiparallel configuration, perpendicularly to their planes of formation by the action of the RKKY interaction, which is facilitated by coupling layer 30 whose effect to couple magnetic moments between adjacent magnetic layers is well known in the art. The designation, using the terms AP1 and AP2 to the two layers, is simply to indicate, by the numeral “1”, the closeness of AP1 to the tunneling barrier layer, 50, which in this example is a layer of MgO formed on layer AP1, but other metal oxides are possible. Layer AP2 is further from layer 50. Next, a ferromagnetic free layer 60 is formed on the tunneling barrier layer; following which a MgO capping layer 70 is formed on the free layer and a hard mask layer 80 is formed on the capping layer, the hard mask layer to be used in subsequent patterning steps of the completed stack. As stated above, these individual layers are successively formed by sputtering processes inside a multi-chamber system in which one chamber is dedicated to cooling the wafer with no sputtering/deposition capability and several other chambers are used for specific sputtering/deposition processes. The cooling process is carried out by transferring the fabrication to the cooling chamber, when cooling is desired, and attaching it by clamps to a metal stage which is temperature-fixed at 60K by flowing Ar gas at that temperature on it. This is illustrated in FIG. 4B below. Cooling of the fabrication occurs quickly by contact with the stage and, in the present process occurs in 200 seconds and stabilizes thereafter. When the cooled temperature is achieved, the fabrication is transferred to the specific separate chamber in which the deposition is to be carried out at ambient. It is noted that the system being used for these processes is commercially available (CANON ANELVA C7100) and it provides for easy transference between the cooling chamber and any one of the deposition chambers. Basically, the system, which is not shown, consists of a central transfer unit from which six satellite chambers radiate out, wherein one satellite chamber provides a cooling facility and the remainder provide facilities for producing various layer depositions. When the fabrication is transferred to the cooling chamber it is clamped to a metal stage on which a good thermal contact is made and the entire fabrication is then cooled by a gas transfer process. When the fabrication reaches the desired temperature, it is removed and transferred to one of the deposition chambers where it is re-fastened to a chuck and the required deposition proceeds while the fabrication remains well within a desired cooled temperature range. Once placed in a chamber in which the deposition process is to occur, the fabrication is no longer being actively cooled so its temperature will slowly rise to ambient. However, because of the slow rise of temperature, the deposition process is effectively carried out on the fabrication at the desired low temperature (60K here). The system and others like it are known in the art, so no further detailed description will be provided herein.

Referring now to FIG. 2, there is schematically illustrated the first step in a series of fabrication processes that are occurring within the multi-chamber system described above within which all processes can be maintained under vacuum and, where necessary, temperature-controlled conditions. Note that each cooling step occurs in the cooling chamber of the system. We begin our description of this exemplary process with the cooling being carried out only at one particular step in the overall fabrication. This single cooling step process can also be applied at other points in the fabrication, and will also be described. In addition, several cooling steps during a single fabrication can also be applied. After the fabrication is affixed to a stage in the cooling chamber (shown in FIG. 4B) and cooled, it is transferred back to a chamber at ambient temperature that is designed for whatever deposition process then occurs. The deposition process is, therefore, applied to the fabrication that is already cold, but is no longer actively being cooled.

Referring back to FIG. 2, a substrate 5 is provided that has been patterned (not shown here) to create a surface region on which the MTJ stack will be fabricated. On this patterned substrate 5, a layer 7 of Ta or the conducting nitride TiN is deposited by sputtering with a thickness of a few hundred Angstroms (A) with 400 A being typical. The surrounding region is filled with SiO2 and the entire region is then smoothed with an oxide CMP process. A seed layer 10 of NiCr between approximately 30 A and 100 A thickness is then deposited on layer 7 which will seed AP2 layer 20, which is a repeated Co/X multilayer, with good lattice growth along the (111) direction. Here X can be chosen from Ni, Pt or Pd, and the individual layers (i.e., Co, X) are typically between approximately 1 A and 10 A in thickness. This multilayered structure will provide PMA (perpendicular magnetic anisotropy) for the entire stack as a result of the repeated interfacial interactions between the layers. In addition, as a result of the RKKY interaction, the AP2 layer will couple anti-ferromagnetically with the AP1 layer, producing oppositely directed magnetic moments perpendicular to their planes of deposition.

Referring now to FIG. 3, we see the deposition of the RKKY interaction layer 30, which may be a layer of Ru of thickness between approx. 3.5 and 4 A, Ir of thickness between approx. 4.5 and 5.5 A or Mo of thickness between approx. 5 and 6 A, which provides the anti-ferromagnetic coupling interaction between the AP2 and AP1 layers that results in an antiparallel orientation of their magnetic moments.

Referring next to FIGS. 4A-4C, there is shown the fabrication of the AP1 layer, which is here formed as the following two layers:

(i) a thin, phase-breaking generally amorphous layer 42 at the bottom to break the (111) crystal structure of the AP2 layer from the (001) crystal structure of the rest of the [AP1/MgO barrier/free layer] structure, while they remain magnetically connected through the RKKY interaction, and

(ii) a CoFeB layer 44 at the top that will contact the MgO barrier layer 50.

Referring first to FIG. 4A there is shown the formation of layer 42, as in (i) above, while the fabrication remains at ambient temperature in the chamber in which layer 30 has been formed.

Referring next to FIG. 4B there is shown the fabrication, now including just-deposited layer 42, transferred to the cooling chamber, wherein the fabrication is placed on a metal stage 3, removably clamped to the stage 4 and cooled by thermal contact to that stage, which is itself cooled by a gas flow 2, to the desired 60K temperature.

Referring now to FIG. 4C, there is shown the cooled fabrication, now shown transferred back to a deposition chamber at ambient temperature, within which layer 44, as in (ii) above, is now deposited.

The fabrication returns very slowly to ambient during deposition so layer 44 is indeed formed on a cold layer 42. The temperature of the wafer will slowly increase, yet during the first few minutes of deposition of the of the rest of the AP1 layer the temperature should not rise very much.

Referring now to FIG. 5, the cooling step is complete and the remaining deposition steps are carried out at ambient temperatures. However, additional cooling steps are still possible, if so desired, but they are not shown here. There is now shown the formation of the MgO tunneling barrier layer 50 on top of CoFeB layer 44. The MgO layer is between 5 and 30 A in thickness. A cooling step can also be applied at this step in the fabrication, before the MgO deposition is completed. Such a cooling step could be in addition to the one previously discussed with the formation of AP1, or it could be done instead of the one performed with the deposition of AP1. Note that the MgO may be formed by sputtering deposition of a Mg layer which is then oxidized or by direct sputtering from a target of MgO.

Referring next to FIG. 6, there is shown the formation of a ferromagnetic free layer 60, generally formed of CoFeB based materials and formed to a thickness of between 5 and 25 A. The cooling step can also be applied before the free layer is deposited or while the free layer is being deposited. If the cooling step is carried out during free layer deposition, the fabrication is removed to the cooling chamber before the free layer is fully deposited. Typically, such a mid-deposition cooling would be done when half of the free layer has been deposited, which would be halfway between a free layer that is generally between 5 and 25 A in thickness. Normally, the free layer is a multi-layered deposition, such as a layer of Fe₇₀B₃₀ followed by a layer of Co₂₀F₆₀B₂₀. In that case, the cooling would occur before deposition of the Co₂₀Fe₆₀B₂₀.

Referring next to FIG. 7, there is shown the deposition of a MgO capping layer 70 on the top of the free layer 60. Again, we note that the MgO may be formed by oxidizing a layer of Mg or by sputtering a layer of MgO. The capping layer is between 5 and 30 A in thickness and the cooling step can be applied after completion of the free layer deposition and before the capping layer deposition. Note that the cooling process can be applied as a series of processes where each cooling step is applied as noted above, before or during each deposition process after first transferring the deposition to the cooling chamber. We note also that the most appropriate fabrication step(s) for applying the cooling process may have to be discovered empirically as the particular nature of the stack seems to affect the beneficial properties of the cooling.

Referring finally to FIG. 8, there is shown the deposition of a hard mask 80 which is formed of Ta of approx. 600 A thickness and that will be used for purposes of patterning the finished stack. We also note that we do not indicate any of the various steps of annealing may be required as dictated by the necessity of integrating the devices into a larger MRAM system. These anneals do not affect the role of the cooling steps nor are they required for setting the magnetization of the RKKY interaction

The beneficial results of this fabrication method can be demonstrated using reflow tests. As shown in the table below, two otherwise identical structures, but one fabricated with and one without a cooling step in forming the AP1 layer of a synthetic antiferromagnetic (SAF) pinned layer (as described below) show different error rates after a reflow process. Reflow is a chip manufacture process where the chip is soldered to the socket by heating a solid layer of solder and causing it to liquify (reflow) and it serves as the strictest requirement for thermal stability of the MTJ stack. Typically, as a result of the reflow process a chip would experience a temperature about 260 C for about 90 s and the information stored in the chip before reflow should not be lost during the process.

Without cooling With cooling Error rate after reflow 10 ppm 1 ppm

The test is done at the wafer level as follows. A wafer that contains more than 50 chips is inserted between two metal slabs inside an oven. The temperature of the metal slabs is at least 260 C and the wafer is inside the oven for at least 90 s. Each chip has 10 Mb MTJ units and was programmed to store either information 0 or 1 before the test. We read each chip after the test to determine the number of MTJ units whose stored information has changed during the baking process. An error rate is then calculated as the number of MTJ units that have changed their information content, divided by the total number of the MTJ devices.

The wafer fabricated without cooling shows an error rate of 10 ppm (10 errors out of 1,000,000 devices) whereas the wafer fabricated with cooing shows an error rate of only 1 ppm. The data clearly indicates significant improvement of PMA of the pinned layer from the proposed cooling step.

As is finally understood by a person skilled in the art, the preferred embodiments of the present invention are illustrative of the present invention rather than limiting of the present invention. Revisions and modifications may be made to methods, materials, structures and dimensions employed in forming and providing an MTJ MRAM cell device using a process that includes cooling the fabrication at various stages, while still forming and providing such a device and its method of formation in accord with the spirit and scope of the present invention as defined by the appended claims. 

What is claimed is:
 1. A method for fabricating an STT MTJ MRAM (Spin Torque Transfer Magnetic Tunneling Junction Magnetic Random Access Memory) cell formed as a sequence of material layers, comprising: providing a patterned substrate; forming a seed layer on the substrate; forming an AP2 layer of an RKKY coupled SAF pinned layer structure on the seed layer; forming an RKKY coupling layer on the AP2 layer; forming a first portion of an AP1 layer on the RKKY coupling layer to form a material stack2; cooling the material stack, wherein cooling includes applying a predetermined temperature to the material stack; forming a second portion of the AP1 layer on the first portion of the AP1 layer, wherein forming of the second portion of the AP1 layer on the first portion of the AP1 layer occurs without maintaining the predetermined temperature; and forming a tunneling barrier layer, a ferromagnetic free layer and a capping layer in that sequential order on the second portion of the AP1 layer.
 2. The method of claim 1 wherein the material layers are formed by sputtering in sputtering chambers of a vacuum sealed multi-chamber system and wherein the cooling occurs in a separate cooling chamber of the system and wherein the material stack is transferred from the sputtering chambers to the cooling chamber for cooling by thermal contact and then returned to the sputtering chambers for the remainder of processing while the material stack returns to an ambient temperature.
 3. The method of claim 1 wherein the material stack is cooled to a temperature of 60K.
 4. The method of claim 1 wherein the seed layer is a layer of NiCr of thickness between 30 and 100 A to facilitate good lattice growth in a (111) direction of the AP2 deposition.
 5. The method of claim 1 wherein the AP2 deposition is a Co/X multilayer where X is selected from the group consisting of Ni, Pt, and Pd.
 6. The method of claim 1 wherein the AP2 deposition provides a PMA (perpendicular magnetic anisotropy) to the entire material stack.
 7. The method of claim 1 wherein the RKKY coupling layer is a layer of material selected from the group consisting of Ru of thickness between approximately 3.5 and 4 A, Ir of thickness between approximately 4.5 and 5.5 A, and Mo of thickness between approximately 5 and 6 A.
 8. The method of claim 1 wherein the AP2 layer has a (111) crystal structure, wherein the second portion of the AP1 layer, tunneling barrier layer, and free layer have a (001) crystal structure, and wherein the first portion of the AP1 layer is a phase breaking layer used to break the respective crystal structures while they remain magnetically connected through the RKKY interaction.
 9. The method of claim 1 wherein the second portion of the AP1 layer is a layer of CoFeB formed to a thickness between 5 and 25 A.
 10. The method of claim 1, wherein without maintaining includes allowing the material stack to return to an ambient temperature.
 11. A method for fabricating a Magnetic Tunneling Junction comprising: providing a substrate; forming a first layer of a pinned structure on the substrate; forming a coupling layer of the pinned structure on the first layer; forming a first portion of a second layer of the pinned structure on the coupling layer to form a material stack; cooling the material stack to a first temperature; after cooling the material stack, forming a second portion of the second layer of the pinned structure on the first portion of the second layer of the pinned structure, wherein forming the second portion of the second layer of the pinned structure on the first portion of the second layer of the pinned structure occurs without maintaining the material stack at the first temperature; forming a tunneling barrier layer on the material stack; and forming a ferromagnetic free layer and a capping layer on the tunneling barrier layer.
 12. The method of claim 11 wherein the material stack is formed by sputtering in sputtering chambers of a vacuum sealed multi-chamber system and wherein the cooling occurs in a separate cooling chamber of the system and wherein the material stack is transferred from the sputtering chambers to the cooling chamber for cooling by thermal contact and then returned to the sputtering chambers for the remainder of processing while the material stack returns to an ambient temperature.
 13. The method of claim 11 wherein the material stack is cooled to a temperature of 60K.
 14. The method of claim 11, wherein without maintaining includes allowing the material stack to return to an ambient temperature.
 15. The method of claim 11 wherein the first layer of the pinned structure is formed of a material selected from the group consisting of Co/Ni, Co/Pt, and Co/Pd, wherein the first layer of the pinned structure has a (111) crystal structure, wherein the coupling layer is formed of a material selected from the group consisting of Ru of thickness between approximately 3.5 and 4 A, Ir of thickness between approximately 4.5 and 5.5 A, and Mo of thickness between approximately 5 and 6 A wherein the second portion of the second layer, tunneling barrier layer, and free layer have a (001) crystal structure, wherein the first portion of the second layer is a phase breaking layer used to break the respective crystal structures while they remain magnetically connected, and wherein a second portion of the second layer is a layer of CoFeB formed on the first portion of the second layer to a thickness between 5 and 25 A.
 16. The method of claim 11 wherein the tunneling barrier layer is formed to a thickness between approximately 5 and 30 A in thickness and wherein the tunneling barrier layer is formed on the material stack by the oxidation of a layer of Mg or by a sputtering deposition using a target of MgO.
 17. A method for fabricating an STT MTJ MRAM (Spin Torque Transfer Magnetic Tunneling Junction Magnetic Random Access) cell formed as a sequence of material layers, comprising: providing a substrate; forming a seed layer on the substrate; forming an RKKY coupled SAF pinned layer structure on the seed layer; forming an MgO tunneling barrier layer on the RKKY coupled SAF pinned layer structure to form a material stack; cooling the material stack, wherein cooling includes applying a first temperature to the material stack; forming a ferromagnetic free layer on the tunneling barrier layer, wherein forming a ferromagnetic free layer on the tunneling barrier layer occurs at a second temperature that is different than the first temperature; and forming a capping layer on the ferromagnetic free layer.
 18. The method of claim 17 wherein the material layers are formed by sputtering in sputtering chambers of a vacuum sealed multi-chamber system and wherein the cooling occurs in a separate cooling chamber of the system and wherein the material stack is transferred from the sputtering chambers to the cooling chamber for cooling by thermal contact and then returned to the sputtering chambers for the remainder of processing while the material stack returns to an ambient temperature.
 19. The method of claim 17 wherein the material stack is cooled to a temperature of 60K.
 20. The method of claim 19 wherein the seed layer is a layer of NiCr of thickness between 30 and 100 A to facilitate good lattice growth in a (111) direction of an AP2 deposition of the RKKY pinned layer structure.
 21. The method of claim 17 wherein the SAF pinned layer comprises an AP2 layer formed as a deposition of Co/X multilayers where X is selected from the group consisting of Ni, Pt, and Pd, wherein an RKKY coupling layer is formed on the AP2 layer, wherein the RKKY coupling layer is formed of material selected from the group including Ru of thickness between approximately 3.5 and 4 A, Ir of thickness between approximately 4.5 and 5.5 A, and Mo of thickness between approximately 5 and 6 A, wherein an AP1 layer having a first portion and a second portion is formed on the RKKY coupling layer, wherein the AP2 layer has a (111) crystal structure, wherein the second portion of the AP1 layer, tunneling barrier layer, and free layer have a (001) crystal structure, wherein the first portion of the AP1 layer is a phase breaking layer used to break the respective crystal structures while they remain magnetically connected through the RKKY interaction, and wherein the second portion of the AP1 layer is a layer of CoFeB formed on the first portion to a thickness between 5 and 25 A.
 22. The method of claim 21 wherein the AP2 deposition provides a PMA (perpendicular magnetic anisotropy) to the entire material stack.
 23. A method for fabricating a Magnetic Tunneling Junction cell comprising: providing a substrate; forming a pinned layer structure on the substrate; forming a tunneling barrier layer on the pinned layer structure to form a material stack; cooling the material stack, wherein cooling includes applying a predetermined temperature to the material stack; after cooling the material stack, forming a ferromagnetic free layer on the material stack, wherein forming the ferromagnetic free layer on the material stack occurs without maintaining the predetermined temperature; and forming a capping layer on the ferromagnetic free layer.
 24. The method of claim 23 wherein the material stack is formed by sputtering in sputtering chambers of a vacuum sealed multi-chamber system and wherein the cooling occurs in a separate cooling chamber of the system and wherein the material stack is transferred from the sputtering chambers to the cooling chamber for cooling by thermal contact and then returned to the sputtering chambers for the remainder of processing while the material stack returns to an ambient temperature.
 25. The method of claim 24 wherein the material stack is cooled to a temperature of 60K.
 26. The method of claim 23 wherein forming the pinned layer structure further comprises: forming a first layer of a material selected from the group consisting of Co/Ni, Co/Pt, and Co/Pd; forming a coupling layer of a material selected from the group consisting of Ru of thickness between approximately 3.5 and 4 A, Ir of thickness between approximately 4.5 and 5.5 A, and Mo of thickness between approximately 5 and 6 A; and forming a second layer in two portions wherein a second portion of the second layer is a layer of CoFeB formed on a first portion of the second layer to a thickness between 5 and 25 A.
 27. The method of claim 26 wherein the first layer deposition provides a perpendicular magnetic anisotropy to the entire material stack.
 28. A method for fabricating an STT MTJ MRAM (Spin Torque Transfer Magnetic Tunneling Junction Magnetic Random Access) cell formed as a sequence of material layers, comprising: providing a substrate; forming a seed layer on the substrate; forming an RKKY coupled SAF pinned layer structure on the seed layer; forming an MgO tunneling barrier layer on the RKKY coupled SAF pinned layer structure; forming a ferromagnetic free layer on the MgO tunneling barrier layer to form a material stack; cooling the material stack, wherein cooling includes applying a predetermined temperature to the material stack; and forming a capping layer on the ferromagnetic free layer, wherein forming the capping layer on the ferromagnetic layer occurs without maintain the predetermined temperature.
 29. The method of claim 28 wherein the material layers are formed by sputtering in sputtering chambers of a vacuum sealed multi-chamber system and wherein the cooling occurs in a separate cooling chamber of the system and wherein the material stack is transferred from the sputtering chambers to the cooling chamber for cooling by thermal contact and then returned to the sputtering chambers for the remainder of processing while the material stack returns to an ambient temperature.
 30. The method of claim 29 wherein the material stack is cooled to a temperature of 60K.
 31. The method of claim 28 wherein the seed layer is a layer of NiCr of thickness between 30 and 100 A to facilitate good lattice growth in a (111) direction of an AP2 deposition of the RKKY pinned layer structure.
 32. The method of claim 28 wherein forming the SAF pinned layer further comprises: forming an AP2 layer having a (111) crystal structure; forming an RKKY coupling layer on the AP2 layer; forming an AP1 layer on the RKKY coupling layer, wherein the AP1 layer includes two portions, wherein an upper portion of the AP1 layer has a (001) crystal structure and wherein a lower portion of the AP1 layer is a phase breaking layer used to break the (111) crystal structure of the AP2 layer from the (001) crystal structure of the upper portion of the AP1 layer.
 33. The method of claim 32 wherein the AP2 deposition provides a PMA (perpendicular magnetic anisotropy) to the entire material stack.
 34. A method for fabricating an STT MTJ MRAM (Spin Torque Transfer Magnetic Tunneling Junction Magnetic Random Access) cell formed as a sequence of material layers, comprising: providing a substrate; forming a seed layer on the substrate; forming an AP2 layer of an RKKY coupled SAF pinned layer structure on the seed layer; forming a RKKY coupling layer on the AP2 layer; forming a first portion of an AP1 layer on the RKKY coupling layer to form a material stack; cooling the material stack for a first time, wherein cooling includes applying a first temperature to the material stack; forming a second portion of the AP1 layer on the first portion of the AP1 layer, wherein forming the second portion of the AP1 layer on the first portion of the AP1 layer occurs while not maintaining the material stack at the first temperature; cooling the material stack for a second time, wherein cooling includes applying the first temperature to the material stack; forming a tunneling barrier layer on the SAF pinned layer wherein forming the tunneling barrier layer occurs while not maintaining the material stack at the first temperature; cooling the material stack for a third time, wherein cooling includes applying the first temperature to the material stack; forming a ferromagnetic free layer on the tunneling barrier layer, wherein forming the ferromagnetic free layer on the tunneling barrier layer occurs while not maintaining the material stack at the first temperature; cooling the material stack for a fourth time, wherein cooling includes applying the first temperature to the material stack; and forming a capping layer on the ferromagnetic free layer, wherein forming the capping layer occurs while not maintaining the material stack at the first temperature.
 35. The method of claim 34 wherein the material layers are formed by sputtering in sputtering chambers of a vacuum sealed multi-chamber system and wherein each of the four cooling processes occurs in a separate cooling chamber of the system and wherein the material stack is transferred from the sputtering chambers to the cooling chamber for cooling by thermal contact and then returned to the sputtering chambers for the remainder of processing while the material stack returns to an ambient temperature.
 36. The method of claim 34 wherein the material stack is cooled to a temperature of 60K during each cooling process.
 37. The method of claim 34 wherein the AP2 layer has a (111) crystal structure, wherein the second portion of the AP1 layer, tunneling barrier layer, and free layer have a (001) crystal structure, and wherein the first portion of the AP1 layer is a phase breaking layer, used to break the respective crystal structures while they remain magnetically connected through the RKKY interaction.
 38. The method of claim 34 wherein the second portion of the AP1 layer is a layer of CoFeB formed to a thickness between 5 and 25 A.
 39. The method of claim 34 wherein the seed layer is a layer of NiCr between 30 and 100 A thick to facilitate good lattice growth in a (111) direction of an AP2 deposition of the RKKY pinned layer structure.
 40. The method of claim 34 wherein the AP2 layer is Co/X multilayer where X is selected from the group consisting of Ni, Pt, and Pd.
 41. The method of claim 34 wherein the AP2 deposition provides a PMA (perpendicular magnetic anisotropy) to the entire material stack. 